过程
|
应用
|
|
FLUONOX®
|
|
比 重
|
氟含量
|
|
收缩温
|
|
|
注 塑
|
|
挤 出
|
压延
|
硬 度
|
|
|
|
|
油封
|
垫圈
|
|
二元氟橡胶
|
|
KB 2252
|
25
|
1.81
|
66
|
18
|
-18 (-0.4)
|
√
|
√
|
√
|
|
√
|
√
|
73
|
13 (1886)
|
260
|
2Y1
|
√
|
|
√
|
|
KB 2253
|
25
|
1.81
|
66
|
17
|
-18 (-0.4)
|
√
|
√
|
√
|
|
√
|
√
|
76
|
14 (2031)
|
200
|
2Y1
|
√
|
|
|
|
KB 2252Z
|
25
|
1.81
|
66
|
25
|
-18 (-0.4)
|
√
|
√
|
√
|
√
|
√
|
√
|
74
|
14 (2031)
|
240
|
2Y1
|
|
√
|
√
|
|
KB 2402
|
40
|
1.81
|
66
|
18
|
-18(-0.4)
|
√
|
√
|
√
|
|
|
|
74
|
14 (2031)
|
250
|
2Y1
|
√
|
|
√
|
|
KB 2403
|
40
|
1.81
|
66
|
17
|
-18(-0.4)
|
√
|
√
|
√
|
|
|
|
77
|
14 (2031)
|
190
|
2Y1
|
√
|
|
|
|
KB 2402Z
|
40
|
1.81
|
66
|
25
|
-18 (-0.4)
|
√
|
√
|
√
|
√
|
|
|
75
|
13 (1886)
|
250
|
2Y1
|
|
√
|
√
|
|
KB 2452
|
45
|
1.81
|
66
|
17
|
-18 (-0.4)
|
√
|
|
|
|
|
|
74
|
14 (2031)
|
250
|
2Y1
|
√
|
|
|
|
KB 2453
|
45
|
1.81
|
66
|
15
|
-18 (-0.4)
|
√
|
|
|
|
|
|
77
|
15 (2176)
|
190
|
2Y1
|
√
|
|
|
|
KB 24527
|
45
|
1.81
|
66
|
25
|
-18 (-0.4)
|
√
|
|
|
√
|
|
|
74
|
14 (2031)
|
250
|
2Y1
|
|
√
|
√
|
|
PessCure 10 min @ 17℃;PostCure: 24 h @ 230℃ (Bisphenen Cure Sstem);4h @ 230℃ (Peroxide Cure System)
|
KB2252：交联含氟弹性体，适合压缩、注入、挤压和压延。
KB2253：交联含氟弹性体，适合压缩、转移、注入、挤出和压延。
KB 2252Z：交联金属粘接型含氟弹性体，适用于压缩、传输、注入、挤压和压延。
KB 2402：交联含氟弹性体，适用于压缩、转移、和注塑。
KB 2403：交联含氟弹性体，适用于压缩、转移和注塑。
KB 2402Z：交联金属粘接型含氟弹性体，适用于压缩、转移和注塑成型。
KB2452：交联含氟弹性体，适用于压缩成型。
KB 2453：交联含氟弹性体，适用于压缩成型。
KB 2452Z：交联金属粘接型含氟弹性体，适用于模压成型。